Butterfly · OFF+
Lin Yun-Ju Super ZLC
5W+2 Super ZLC · Outer
Specifications
- Playing style
- OFF+
- Price
- Not published
- Weight
- 84 g
- Thickness
- 5.6 mm
- Plies
- 7
- Composition
- 5W+2 Super ZLC
- Outer ply
- Koto
- Core wood
- Kiri
- Carbon type
- Super ZLC
- Fibre placement
- Outer
- Blade size
- 157 × 150 mm
- Handle types
- FL · AN · ST
- Made in
- Not published
- Release year
- Not published
Metadata confidence: Specialist measured
Blade construction
Verified5W+2 Super ZLC · Outer
7 plies · Koto surface · Super ZLC outer fibre · Kiri core · 5.6 mm total
One blade, drawn as technical linework at real shakehand proportions. The laminated edge along the crown and right rim exposes every ply boundary in the stack. Edge depth is illustrative because physical veneer thickness is not published.
Stack order · outer face to outer face
1 · Outer ply
Koto
2 · Fibre layer
Super ZLC
3 · Medial ply
Ayous
4 · Core
Kiri
5 · Medial ply
Ayous
6 · Fibre layer
Super ZLC
7 · Outer ply
Koto
Koto
Outer ply · layers 1 and 7
Crisp, direct hit · Speed off the bounce
Super ZLC
Fibre layer · layers 2 and 6
Stiffest fibre · Hard catapult
Ayous
Medial ply · layers 3 and 5
Lower weight · Wider sweet spot
Kiri
Core · layer 4
Lower weight · Controlled rebound
Stack order — face A to face B
- 01KotoOuter ply
Hard, dense outer veneer — a crisp, direct hit and plenty of speed straight off the bounce.
- 02Super ZLCFibre layer
High-density zylon-carbon — the stiffest, fastest of the fibre families with a hard catapult.
- 03AyousMedial ply
Very light medial or core wood — keeps the blade low in weight and widens the sweet spot.
- 04Kiri — coreCore
Paulownia core — extremely light, damping the stack and slowing the blade down for control.
- 05AyousMedial ply
Very light medial or core wood — keeps the blade low in weight and widens the sweet spot.
- 06Super ZLCFibre layer
High-density zylon-carbon — the stiffest, fastest of the fibre families with a hard catapult.
- 07KotoOuter ply
Hard, dense outer veneer — a crisp, direct hit and plenty of speed straight off the bounce.
Specialist measured · 7 of 7 plies with published material · stack order confirmed
About this blade
Butterfly Lin Yun-Ju Super ZLC is a 7-ply blade built around Super ZLC fibre placed outer, with Koto on the playing surface and a Kiri core. Koto in the outer layer: Hard, dense outer veneer — a crisp, direct hit and plenty of speed straight off the bounce. Ayous in the medial layer: Very light medial or core wood — keeps the blade low in weight and widens the sweet spot. Kiri in the core: Paulownia core — extremely light, damping the stack and slowing the blade down for control. Super ZLC in the fibre layer: High-density zylon-carbon — the stiffest, fastest of the fibre families with a hard catapult. Physically it measures 5.6 mm thick, around 84 g. Butterfly positions it for off+ play.
TTDNA ratings
NormalizedPerformance
Construction
Material properties
Playing profile
A TTDNA blade rating measures how much of the named characteristic a blade has. For descriptive rows — flex, stiffness, vibration, head heaviness, weight, thickness, carbon feel, softness, technique requirement, spin sensitivity — a higher number means more, not better.
TTDNA ratings are normalized comparison values, not laboratory measurements. They are built from published specifications, technical sources and structured product evidence, converted to one 0–100 scale. Where a directly comparable measurement is unavailable, the value is an evidence-based estimate. Overall-style scores are composites of several characteristics. Methodology